GER-N27L iyo GER-N27 ee aanu soo saarno labaduba waa birta birta ah ee heerkulka hooseeya ee sodium-dahaarka leh oo leh Ni content 2.5%, kuwaas oo inta badan loo isticmaalo alxanka ASME SA-203 GRA/B iyo 09MnNiDR birta. Moodooyinka GER-N27L iyo GER-N27 ee hadda fulinaya GB/T5117-2012 waa E5015-N5 P/E5015-G P iyo E5515-N5 P siday u kala horreeyaan, kuwaas oo u dhigma darajooyinka "Buugga Alaabta Alaabta Alxanka" ee ay daabacday Machinery Saxaafadda Warshadaha. W707 iyo W707Ni, sifooyinka jidheed iyo kiimikaad ee birta kaydsan ee labada electrodes ayaa la barbardhigay sida soo socota.
| Magaca | Qaabka | Qaybaha kiimikada% | |||||
| C | Mn | Si | Ni | S | P | ||
| GER-N27L | E5015-N5P/ E5015-GP (W707) | ≤0.05 | ≤1.25 | ≤0.50 | 2.00-2.75 | ≤0.03 | ≤0.03 |
| GER-N27 | E5515-C1 (W707Ni) | ≤0.12 | ≤1.25 | ≤0.60 | 2.00-2.75 | ≤0.03 | ≤0.03 |
| Magaca | Qaabka | Guryaha makaanikada iyo haydarojiin la faafin karo | |||||
| PWHT | Rm (Mpa) | Rel (Mpa) | A (%) | KV2 (j) | H (ml/100g) | ||
| GER-N27L | E5015-N5P/ E5015-GP (W707) | 605 ±15℃*h | ≥490 | ≥390 | ≥22 | -75 ℃ KV2≥27 | ≤5 |
| GER-N27 | E5515-C1 (W707Ni) | ≥540 | ≥440 | ≥17 | -60℃ KV2≥27 | ||
Waxaa laga arki karaa shaxda kore in isku dhafka kiimikada C iyo Si ee birta kaydsan ee GER-N27 (W707Ni) ay waxyar ka sarreeyaan kuwa GER-N27L (W707). Sidaa darteed, marka la eego xoogga, GER-N27L (W707) waxay ka tirsan tahay korantada darajada 490MPa oo leh quwad jilicsan oo hooseeya. GER-N27 (W707Ni) waa heer, iyo waxqabadka saamaynta GER-N27L (W707) u dhiganta waa wax yar ka fiican GER-N27 (W707Ni), laakiin codsiyada la taaban karo, GER-N27L (W707) iyo GER-N27 ( W707Ni) Saamaynta Imtixaanka guud ahaan waa la aqbalay iyadoo loo eegayo tusmada -70°C ama -75°C.
① Kahor inta aan la jarin
② Ka dib marka la gooyo
GER-N27L (W707) alxanka suufka toosan
① Kahor inta aan la jarin
② Ka dib marka la gooyo
GER-N27 (W707Ni) alxanka suufka toosan
GER-N27L iyo GER-N27 waxay leeyihiin meel wanaagsan oo dhan alxanka marka alxanka ASME SA-203 GrA/B ama 09MnNiDR steel (sida ku cad shaxanka kor ku xusan ee formation of tolmo alxanka toosan ee labada electrodes), iyo guud ahaan waa. Waxaa lagu taliyay in tamarta xariiqda alxanka aysan ka badneyn 35kJ/cm, si loo helo qaab dhismeed aad u wanaagsan oo ay maamusho ferrite acicular. Marka GER-N27L (W707) lagu dabaqo qalabka u baahan deminta iyo daawaynta kulaylka + annealing daaweynta kulaylka, sida caadiga ah waa in la helo adag saamayn heerkulka hoose ka wanaagsan, laakiin waxa ay lumin doontaa xoogaa xoog ah, iyo xoogga xajintu guud ahaan waa ka hooseeyaa. 500MPa; GER-N27L (W707) Marka laga soo tago munaaradaha, waxaa sidoo kale loo isticmaalaa 09MnNiDR birta ethylene taangiyada, halka GER-N27 (W707Ni) inta badan lagu isticmaalo weelasha heerkulka hoose oo kaliya u baahan daaweynta kulaylka. Kuwa soo socdaa waxay ku siin doonaan tusaalayaal codsiga iyo waxqabadka la xidhiidha GER-N27L iyo GER-N27 .
| Ulaha alxanka | Magaca aaladda | Daaweynta kulaylka iyo shuruudaha farsamada | Xogta la qiyaasay |
| GER-N27L (E5015-G) | 09MnNiDR munaaradda nuugista gaaska shift | Caadiyan 915 ± 15 ℃ * 1.5h qaboojinta hawada + heerkulka 645 ± 15 ℃ * 2.5h qaboojinta hawada + 615 ± 15 ℃ * 10h Ka dib marka foornada la qaboojiyo: Rel≥300MPa Rm≥440MPa A%≥23 -70 ℃KV2≥60J Hardness HV10≤220 | Rel=347MPa Rm=462MPa A=37% -70℃KV2=255J Adag HV10=151 |
| GER-N27L (E5015-N5P) | 09MnNiDR Taangiga wareegsan ee Vinyl | 580± 15 ℃ * 4 saac Ka dib marka foornada la qaboojiyo: Rel≥390MPa Rm≥490MPa A%≥22 -70 ℃KV2≥54J | Rel=456MPa Rm=538MPa A=27% -70℃KV2=139J |
| GER-N27 (E5515-N5P) | 09MnNiDR weelka cryogenic | Ugu yaraan PWHT: 590± 15℃*3.5h Ka dib marka foornada la qaboojiyo: Ugu badnaan PWHT: PWHT590± 15℃*16.5h Rel≥440MPa Rm≥540MPa A%≥17 -70 ℃KV2≥54J | Ugu yaraan PWHT: Rel=477MPa Rm=570MPa A=26% -70℃KV2=108J |
| Ugu badnaan PWHT: Rel=476MPa Rm=566MPa A=28.5% -70℃KV2=112J |
09MnNiDR munaaradda nuugista
09MnNiDR haanta wareega ee ethylene